1.  Kúdela Jr S., Švec P., Bajana O., Orovčík L., Ranachowski P., Ranachowski Z., Saffil alumina fibers reinforced dual-phase Mg-Li and Mg-Li-Zn alloys, KOVOVE MATERIALY-METALLIC MATERIALS, ISSN: 0023-432X, DOI: 10.4149/km_2017_3_195, Vol.55, No.3, pp.195-203, 2017

Streszczenie:
The gas pressure infiltration technique was used to prepare Saffil alumina fibers reinforced Mg-Li and Mg-Li-Zn matrix composites with a dual-phase matrix structure. There was investigated the effect of variable Li content (6.2–10.3 wt.% Li) and Zn alloying (∼ 1.5 wt.% Zn) on the proof stress Rp0.2 of prepared composites. Rp0.2 values increased monotonously with rising fraction of Saffil fibers (5, 10 and 15 vol.%) reaching the maximum of about 250 MPa for Mg-Li matrix composites. Rp0.2 values of Mg-Li-Zn matrix composites were lower. Strengthening effect of Saffil fibers was promoted by the displacement redox reaction with Mg-Li and Mg-Li-Zn melts in which only Li significantly participated. Zn alloying retarded the displacement redox reaction. Too extensive reaction, however, resulted in the fiber damage and the drop in composite strength.

Słowa kluczowe:
Mg-Li alloys, Saffil fibers, metal matrix composites, short-fiber strengthening, reactive wetting, displacement reactions

Afiliacje autorów:
Kúdela Jr S. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Švec P. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Bajana O. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Orovčík L. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Ranachowski P. - IPPT PAN
Ranachowski Z. - IPPT PAN
20p.
2.  Kúdela Jr S., Švec P., Bajana O., Orovčík L., Ranachowski P., Ranachowski Z., Strengthening in dual-phase structured Mg-Li-Zn alloys, KOVOVE MATERIALY-METALLIC MATERIALS, ISSN: 0023-432X, DOI: 10.4149/km_2016_6_483, Vol.54, pp.483-489, 2016

Streszczenie:
Proof stress Rp0.2 of dual-phase α + β structured Mg-Li and Mg-Li-Zn alloys has been inspected in terms of the strengthening contributions of α- and β-phases. The alloys studied with a variable fraction of α- and β-phases have been subjected to compression straining tests, microhardness measurements and structural analysis by EDX and XRD. Alloying with 1.5 wt.% Zn results in the hardening of both α- and β-phases which however exhibit different hardening responses due to different Zn enrichment. The rule of the mixture has been used to interpret Rp0.2 values by taking into account the fraction of α- and β-phases and their strength level represented by their microhardness. Compression stress-strain curves indicate that work hardening of alloys studied depends considerably on the fraction of α-phase and is higher for Zn-containing alloys.

Słowa kluczowe:
Mg-Li, Mg-Li-Zn, dual-phase alloy, solution hardening, ageing, work hardening

Afiliacje autorów:
Kúdela Jr S. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Švec P. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Bajana O. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Orovčík L. - Institute of Materials and Machine Mechanics, Slovak Academy of Sciences (SK)
Ranachowski P. - IPPT PAN
Ranachowski Z. - IPPT PAN
20p.

Kategoria A Plus

IPPT PAN

logo ippt            ul. Pawińskiego 5B, 02-106 Warszawa
  +48 22 826 12 81 (centrala)
  +48 22 826 98 15
 

Znajdź nas

mapka
© Instytut Podstawowych Problemów Techniki Polskiej Akademii Nauk 2024