1.  Gradys A., Sajkiewicz P., Adamovsky S., Minakov A.A., Schick C., Crystallization of poly(vinylidene fluoride) during ultra-fast cooling, THERMOCHIMICA ACTA, ISSN: 0040-6031, DOI: 10.1016/j.tca.2007.05.023, Vol.461, pp.153-157, 2007

Streszczenie:
Melt-crystallization of polyvinylidene fluoride (PVDF) was investigated in non-isothermal mode at ultra-high cooling rates ranging between 30–3000 K/s as well as at constant temperatures after quenching at 6000 K/s. An increase of the cooling rate above 150 K/s leads to the formation of betaphase manifested by a low temperature shoulder of crystallization exotherm in addition to the alphamodification. At the cooling rates above 2000 K/s there is only low temperature exothermic peak that is attributed to the crystallization of pure betamodification. Isothermal crystallization was possible to realize at 110 oC as the lowest, resulting in form. Much higher crystallization rate in submicrogram samples, as compared to standard DSC experiments, is also reported.

Słowa kluczowe:
Polyvinylidene fluoride, Crystallization, Ultra-fast calorimetry, Polymorphism

Afiliacje autorów:
Gradys A. - IPPT PAN
Sajkiewicz P. - IPPT PAN
Adamovsky S. - Universität Rostock (DE)
Minakov A.A. - inna afiliacja
Schick C. - University of Rostock (DE)
2.  Gradys A., Sajkiewicz P., Minakov A.A., Adamovsky S., Schick C., Hashimoto T., Saijo K., Crystallization of polypropylene at various cooling rates, MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, ISSN: 0921-5093, DOI: 10.1016/j.msea.2005.08.167, Vol.413-414, pp.442-446, 2005

Streszczenie:
Crystallization of polypropylene (PP) can result in formation of different crystal modifications depending on external conditions. The mechanisms of formation of various crystal modifications in polypropylene are still under discussion.We have investigated non-isothermal melt crystallization of isotactic polypropylene at cooling rates ranging from 1 up to 180,000 K/min using two types of differential scanning calorimeters-standard device Perkin–Elmer DSC Pyris-1 and ultra-fast calorimeter. Additional results were obtained by means of wide angle X-ray scattering and optical microscopy. At cooling rates below 6000 K/min there is only one exothermic peak corresponding to simultaneous crystallization ofalpha andbeta modifications. At cooling rates higher than 6000 K/min there is additional low temperature DSC peak corresponding to formation of mesomorphic phase. At the rates higher than 36,000 K/min there is no trace of formation of any ordered phase. In our opinion this complex behavior observed during crystallization of polypropylene can be explained using the concept of metastable phases. An increase ofbeta content in samples with quinacridone pigment has been observed only at very low cooling rates, corresponding to high temperatures of crystallization and low homogeneous nucleation rate.

Słowa kluczowe:
Polypropylene, Crystallization, Utra-fast calorimetry, Crystallographic modifications, Metastable phases

Afiliacje autorów:
Gradys A. - IPPT PAN
Sajkiewicz P. - IPPT PAN
Minakov A.A. - inna afiliacja
Adamovsky S. - Universität Rostock (DE)
Schick C. - University of Rostock (DE)
Hashimoto T. - inna afiliacja
Saijo K. - inna afiliacja

Kategoria A Plus

IPPT PAN

logo ippt            ul. Pawińskiego 5B, 02-106 Warszawa
  +48 22 826 12 81 (centrala)
  +48 22 826 98 15
 

Znajdź nas

mapka
© Instytut Podstawowych Problemów Techniki Polskiej Akademii Nauk 2021