1.  Chmielewski M., Nosewicz S., Jakubowska D., Lewandowska M., Mizera J., Rojek J., Bazarnik P., The influence of sintering time on the microstructural properties of chromium-rhenium matrix composites, International Journal of Refractory Metals and Hard Materials, ISSN: 0263-4368, DOI: 10.1016/j.ijrmhm.2016.05.017, Vol.59, pp.78-86, 2016

Streszczenie:
This paper comprises the results of studies of the changes in the structure of Cr-Re-Al2O3 metal matrix depending on heat treatment time in sintering temperature. The density of material with the following composition: 95%(75%Cr-25%Al2O3)+5%Re was increased using the technique of sintering under pressure (30MPa) at the temperature of 1450°C. As a result, materials characterized by a high relative density (< 97% of theoretical density) were obtained. Next, they were subjected to structural tests including scanning and transmission electron microscopy as well as X-ray diffraction. Changes in the phase composition, grains size and parameters of crystallographic structure depending on heat treatment time were analysed. It was found that during sintering rhenium is dissolved in the chromium matrix and Cr-Re solid solution is formed. When sintering time is extended to 120 min, the matrix of the composite becomes completely homogenous, which results in an increased strength of the composite.

Słowa kluczowe:
Metal matrix composites, Rhenium, Hot pressing, Microstructure analysis, XRD

Afiliacje autorów:
Chmielewski M. - Institute of Electronic Materials Technology (PL)
Nosewicz S. - IPPT PAN
Jakubowska D. - inna afiliacja
Lewandowska M. - inna afiliacja
Mizera J. - Warsaw University of Technology (PL)
Rojek J. - IPPT PAN
Bazarnik P. - Warsaw University of Technology (PL)
35p.

Kategoria A Plus

IPPT PAN

logo ippt            ul. Pawińskiego 5B, 02-106 Warszawa
  +48 22 826 12 81 (centrala)
  +48 22 826 98 15
 

Znajdź nas

mapka
© Instytut Podstawowych Problemów Techniki Polskiej Akademii Nauk 2021