1.  Gorniewicz D., Przygucki H., Kopeć M., Karczewski K., Jóźwiak S., TiCoCrFeMn (BCC + C14) high-entropy alloy multiphase structure analysis based on the theory of molecular orbitals, Materials, ISSN: 1996-1944, DOI: 10.3390/ma14185285, Vol.14, No.18, pp.5285-1-16, 2021

High-entropy alloys (HEA) are a group of modern, perspective materials that have been intensively developed in recent years due to their superior properties and potential applications in many fields. The complexity of their chemical composition and the further interactions of main elements significantly inhibit the prediction of phases that may form during material processing. Thus, at the design stage of HEA fabrication, the molecular orbitals theory was proposed. In this method, the connection of the average strength of covalent bonding between the alloying elements (Bo parameter) and the average energy level of the d-orbital (parameter Md) enables for a preliminary assessment of the phase structure and the type of lattice for individual components in the formed alloy. The designed TiCoCrFeMn alloy was produced by the powder metallurgy method, preceded by mechanical alloying of the initial elementary powders and at the temperature of 1050 °C for 60 s. An ultra-fine-grained structured alloy was homogenized at 1000 °C for 1000 h. The X-ray diffraction and scanning electron microscopy analysis confirmed the correctness of the methodology proposed as the assumed phase structure consisted of the body-centered cubic (BCC) solid solution and the C14 Laves phase was obtained.

Słowa kluczowe:
HEA, solid solution, laves phase, U-FAST sintering

Afiliacje autorów:
Gorniewicz D. - Military University of Technology (PL)
Przygucki H. - GeniCore Sp. z o.o. (PL)
Kopeć M. - IPPT PAN
Karczewski K. - Military University of Technology (PL)
Jóźwiak S. - Military University of Technology (PL)

Abstrakty konferencyjne
1.  Górniewicz D., Jóźwiak S., Przygucki H., Kopeć M., The concept of improving the fracture toughness of double-phase high entropy alloy produced by high-pulse sintering method U-FAST, BSSM, 15th International Conference on Advances in Experimental Mechanics, 2021-09-07/09-09, Swansea (GB), pp.1-2, 2021

In this paper, double-phase high entropy alloys with the BCC solid solution matrix and the C14 structured intermetallic Laves phase precipitates with the were obtained. The mixture of Co, Cr, Fe, Mn, Ti and CuO powders was sintered at 1000°C for 1 min using innovative high-pulse sintering U-FAST method. Such method allows to obtain complex TiCoCrFeMn and TiCoCrFeMn+5 vol.% CuO double-phase high entropy alloys. The followed annealing process led to the significant improvement of the fracture toughness of 46 % for TiCoCrFeMn alloy and 27 % for TiCoCrFeMn+5vol.%CuO alloy.

Afiliacje autorów:
Górniewicz D. - Military University of Technology (PL)
Jóźwiak S. - Military University of Technology (PL)
Przygucki H. - GeniCore Sp. z o.o. (PL)
Kopeć M. - IPPT PAN

Kategoria A Plus


logo ippt            ul. Pawińskiego 5B, 02-106 Warszawa
  +48 22 826 12 81 (centrala)
  +48 22 826 98 15

Znajdź nas

© Instytut Podstawowych Problemów Techniki Polskiej Akademii Nauk 2024